Perforated clay brick
FROST
CERAMICA MALPESA
Facing bricks manufactured by extruding a mixture of special clays and water. After drying off the water added for the extrusion, the bricks are fired in an oxidizing atmosphere in a Tunnel Kiln until they acquire high density, low water absorption and suction (initial rate of absorption) and high compressive strength. These bricks are particularly attractive and naturally longlasting. They are ideal for harsh environments.
Measures: 23.6 cm 11.3 cm 4.9 cm
Texture: Smooth
Weight aprox: 1,75 Kg.
Water absorption: ≤ 6 %
Suction, Kg / (m2-min) ≤ 0,9
Char. norm. compression resistance: ≥40,0 N/mm2
Durability (Frosting) F2
Thermal properties (λeq) 0,401 W/mK
Humidity expansion ≤ 0,50 mm/m
Reaction to fire Clase A1
Measures: 23.6 cm 11.3 cm 4.9 cm
Texture: Smooth
Weight aprox: 1,75 Kg.
Water absorption: ≤ 6 %
Suction, Kg / (m2-min) ≤ 0,9
Char. norm. compression resistance: ≥40,0 N/mm2
Durability (Frosting) F2
Thermal properties (λeq) 0,401 W/mK
Humidity expansion ≤ 0,50 mm/m
Reaction to fire Clase A1