FIRE REACTION (EUROCLASSES) UNE-EN-ISO 9239-1:2002 & ISO 1716:2002 - Euroclassses - A2fl s1
LINEAR THERMAL EXPANSION COEFFICIENT UNE EN 14617-11:2006 - ºC-1 - 14,8-26,4X10e-6
FLEXURAL STRENGTH UNE EN 14617-2:2005 - MPa - 24,3 – 30,1
IMPACT RESISTANCE UNE EN 14617-9:2005 - J - 3 – 6
SLIP RESISTANCE UNE EN 14231:2004 - USRV - Polish: 5-6 wet / 44-60 dry Silken: 21 wet / 55 dry
WATER ABSORPTION UNE EN 14617-1:2005 - % - 0,041 – 0,105
COMPRESSION RESISTANCE UNE EN 14617-15:2005 - MPa - 130,6 – 137,0
APPARENT DENSITY UNE EN 14617-1:2005 - g/cm3 - 2,45 – 2,49
ABRASION RESISTANCE UNE-EN 14617-4:2005 - mm - 33 – 36
CHEMICAL RESISTANCE UNE EN 14617-10: 2005 - C1 C4 - Acid: C1 (material which keeps below 60% of the reflection reference value after 8h of acid attack) Alkali: C4 (material keeps at least 80% of the reflection reference value after 8h of acid or basis attack)
SURFACE HARDNESS UNI EN 101 Ceramic tiles. - MOHS - 3 – 4